Width, mm | 10 … 1650, ± 0.2 % |
Thickness, micron | 30 …150, ± 10 % |
Logo | 4 colors, Varnish / Intercoat |
Antistatic | On demand |
Antislip | On demand |
Dyeing | On demand |
Adhesion, g * | 50-80 |
Surface type / feature | Gloss |
Variations | Available in Low, Middle and High variations |
The foundation | PE |
Glue type | acrylic |
Overall thickness, microns | Not less than 35 |
* Tensile strength, MPa, not less, MD / CD | 14,7/13,7 |
* Relative elongation at break,%, not less, MD / CD | 110/200 |
Transport and storage | t = 15 … 30 degrees С φ = 40 … 75 % |
Application for n / a | t = 15 … 60 град. С φ = 40 … 75 % |
Application for extreme conditions. | t = 105 град. С φ = 85 % |
Determination of peeling adhesion according to ASTM D 3330
* Elongation at break characterizes the change in the initial length of the film when stretched to the moment of rupture.
* Tensile Strength: The maximum load per unit of width observed during a test in which the specimen is stretched to break.
The film is applied in production and must be removed after installation.
The film is applied to the protected surface both manually and mechanically. For mechanical application to the surface - the lines must be equipped with a special roller system for applying the film before the material is shaped and cut.
Before use, the film is kept for at least 3 hours at a temperature of 15 - 30 ° C. Remove the label from the roll immediately before using the film and store it until the end of the roll.
The film must be applied without wrinkles and air bubbles to avoid problems during further surface treatment or transportation of the finished product.
It is recommended to carry out lamination at temperatures from +15 to + 40 degrees. WITH
The film is transported by any type of covered transport in accordance with the rules for the carriage of goods in force for a specific type of transport. Transportation conditions are in accordance with GOST 15150.
The film should be stored in closed dry rooms, excluding direct sunlight, at a distance of at least 1 m from heating devices. Store in its original packaging at a temperature of 15-25 ° C and a relative humidity of 40-60%.
It is not allowed to store the film with organic solvents, flammable and combustible liquids, acids, chemicals and other aggressive media.
The film should be removed no more than a year from the date of lamination, or after 3 months if the product was exposed to natural factors and provided there was no direct contact with water.